掺碲硒化镓晶体的光学性能

1.
国立交通大学, 新竹 30010, 中国台湾;
2.
俄罗斯科学院西伯利亚分院气候与生态系统监测研究所, 托木斯克 634055, 俄罗斯;
3.
俄罗斯托木斯克洲立大学西伯利亚物理技术研究所, 托木斯克 634050, 俄罗斯;
4.
中国科学院长春光学精密机械与物理研究所, 吉林长春 130033

基金项目:

supported by RFBR Project(No.10-02-01452-a), Presidium SB RAS under the Project VII.63.3.1 of VII.63.3 Prog. and Join Proj. between Presidium SB RAS and Presidium NAS, Belarus No.10 of 2010.

详细信息

中图分类号:O734; TN304.2
计量
- 文章访问数:3378
- HTML全文浏览量:359
- PDF下载量:1214
- 被引次数:0
出版历程
- 收稿日期:2011-09-21
- 修回日期:2011-11-23
- 刊出日期:2011-12-25

Optical properties of Te-doped GaSe crystal

1.
National Chiao Tung University, Hsinchu 30010, Taiwan, China;
2.
Institute of Monitoring of Climatic and Ecological System SB RAS, Tomsk 634055, Russia;
3.
Siberian Physics-technical Institute of TSU, Tomsk 634050, Russia;
4.
Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, Changchun 130033, China

Funds:

supported by RFBR Project(No.10-02-01452-a), Presidium SB RAS under the Project VII.63.3.1 of VII.63.3 Prog. and Join Proj. between Presidium SB RAS and Presidium NAS, Belarus No.10 of 2010.

More Information

Author Bio:
KU Shin-an(1985-), Post-graduate student, National Chiao Tung University, Taiwan, China. His research interests include nonlinear optics and THz spectroscopy. E-mail:ksa7471@hotmail.com CHU Wei-chen(1989-), Master Student, National Chiao Tung University, Taiwan, China. Her research interests include nonlinear optics and THz spectroscopy. E-mail:s.daffodil@hotmail.com
KU Shin-an(1985-), Post-graduate student, National Chiao Tung University, Taiwan, China. His research interests include nonlinear optics and THz spectroscopy. E-mail:ksa7471@hotmail.com CHU Wei-chen(1989-), Master Student, National Chiao Tung University, Taiwan, China. Her research interests include nonlinear optics and THz spectroscopy. E-mail:s.daffodil@hotmail.com

摘要

摘要:采用水平区熔法生长了碲(Te)掺杂浓度(质量百分比)分别为0.05%,0.1%,0.5%,1%,2%的硒化镓(GaSe)晶体,并分别对掺杂浓度为0.01%,0.07%,0.38%,0.67%,2.07%的GaSe∶Te晶体的光学性能进行了表征。首次研究了GaSe∶Te晶体中刚性层声子模式的转换。吸收光谱测试结果表明:当Te掺杂浓度小于0.38%时,振动中心位于0.59 THz附近的E'(2)刚性模式吸收峰强度可达最大值,这一过程与GaSe∶Te晶体光学性能的提高密切相关。但Te掺杂浓度的进一步提高会导致E'(2)刚性模式吸收峰强度逐渐减弱,当Te掺杂浓度为1%时,E'(2)刚性模式吸收峰基本消失。这两个过程与GaSe∶Te晶体光学质量的下降密切相关。因此,E'(2)刚性模式吸收强度达到最高时对应的掺杂浓度即是GaSe∶Te晶体中Te的最佳掺杂浓度,光整流产生太赫兹过程证实了此结论的正确性。
- 硒化镓/
- 掺碲硒化镓/
- 晶体生长/
- 光学性能/
- 太赫兹
Abstract:-GaSe crystals are grown with the stoichiometric GaSe of 0.05%, 0.1%, 0.5%, 1% and 2%(mass percent) Te and are characterized by GaSe∶Te(0.01%, 0.07%, 0.38%, 0.67% and 2.07%(mass percent)) crystals. The transformation of the rigid layer phonon modes with doping is studied for the first time. The absorption peak of the rigid mode E'(2) centered at ~0.59 THz is rising up in the intensity till reaching a maximal value on the first stage of the doping concentration less than 0.38%(mass percent). This process correlates well with the improvement in the optical property. Further doping is resulting in the decrease of the intensity till vanishing the E'(2) absorption peak at 1%(mass percent) Te. Simultaneously with the E'(2) absorption peak decreasing, the absorption peak of the rigid mode E'(2) centered at 1.78 THz is rising up in the intensity. The two processes correlate well with the degradation in the optical quality of GaSe∶Te crystal. The doping level that results in the highest intensity of the absorption peak of the rigid layer mode E'(2) is proposed as a criterion in the identification of the optimal Te-doping in GaSe crystal that is confirmed by THz generation via optical rectification.
- Te crystal/
- crystal growth/
- optical property/
- THz/

HTML全文

参考文献 (1)

[1] DMITRIEV V G,GURZADYAN G G,NIKOGOSYAN D N.Handbook for Nonlinear Optical Crystals[M]. 3rd ed. Berlin:Springer,1999. [2] LEE Y S.Principles of Terahertz Science and Technology[M]. Berlin:Springer,2008. [3] ALLAKHVERDIEV K R,GULIEV R I,SALAEV E Y,et al.. Investigation of linear and nonlinear optical properties of GaS_xSe_1-xcrystals[J].Sov. J. Quantum Electron.,1982,12:947-948. [4] SUHRE D R,SINGH N B,BALAKRISHNA V,et al.. Improved crystal quality and harmonic generation in GaSe doped with indium[J].Opt. Lett.,1997,22:775-777. [5] SINGH N B,SUHRE D R,ROSCH W,et al.. Modified GaSe crystals for mid-IR applications[J].J. Cryst. Growth,1999,198:588-592. [6] HSU Y K,CHEN C W,HUANG J Y,et al.. Erbium doped GaSe crystal for mid-IR applications[J].Opt. Express,2006,14:5484-5491. [7] FENG Z S,KANG Z H,WU F G,et al.. SHG in doped GaSe∶In crystals[J].Opt. Express,2008,16:9978-9985. [8] ZHANG H Z,KANG Z H,JIANG Y,et al.. SHG phase matching in GaSe and mixed GaSe_1-xS_{x,x≤0.412, crystals at room temperature[J].Opt. Express,2008,16:9951-9957. [9] RAK Z,MAHANTI S D,MANDAL K C,et al.. Doping dependence of electronic and mechanical properties of GaSe_1-xTe_xand Ga_1-xIn_xSe from first principles[J].Phys. Rev. B,2010,82:155203. [10] SHI W,DING Y J. A monochromatic and high-power terahertz source tunable in the ranges of 2.7~38.4 and 58.2~3540 μm for variety of potential applications[J].Appl. Phys. Lett.,2004,84:1635-1637. [11] DING Y J,SHI W. Widely tunable monochromatic THz sources based on phase-matched difference-frequency generation in nonlinear-optical crystals:a novel approach[J].Laser Phys.,2006,16:562-570. [12] ATUCHIN V V,ANDREEV Y M,SARKISOV S Y,et al.. GaSe_1-xS_xcrystals for terahertz frequency range[C]//10^thAnnual International Conference and Seminar on Micro/Nanotechnologies and Electron Devices(EDM 2009),July 1-6,2009,Novosibirsk Tomsk,Russia,2009:96-99. [13] ANDREEV Y M,BEREZNAYA S A,VINNIK E M,et al.. Optical properties of GaSe_1-xS_xin THz range[C]//Eight Siberian Conference on Climate and Ecological Monitoring,Oct 8-10,2009,Tomsk,Russia,2009:375-376.(in Russian) [14] LUO Z W,GU X A,ZHU W C,et al.. Optical properties of GaSe∶S crystals in terahertz frequency range[J].Opt. Precision Eng.,2011,19:354-359.(in Chinese) [15] ANDREEV Y M,LANSKII G V,ORLOV S N,et al.. Physical properties, phase matching and frequency conversion in GaSe_1-xS_x, Ga_1-xIn_xSe and GaSe_1-xTe_x[C]//17^thInt. Conf. on Advanced Laser Technologies,Sept 26-Oct 1,2009,Antalya,Turkey,2009. [16] SARKISOV S Y,NAZAROV M M,TOLBANOV O P,et al.. Generation and detection of THz pulsed radiation by GaSe GaSe, GaSe_1-xTe_x, GaSe_1-xS_x, crystals[C]//IX Russian Conf. on Semiconductor Physics,Sept 28-Oct 3,2009,Novosibirsk Tomsk,Russia,2009.(in Russian) [17] ZHANG L M,GUO J,LI D J,et al.. Dispersion properties of GaSe_1-xS_xin the terahertz range[J].J. Appl. Spectr.,2011,77:850-856. [18] MANDAL K C,KANG S H,CHOI M,et al.. III VI chalcogenide semiconductor crystals for broadband tunable THz sources and sensors[J].IEEE J. Sel. Top. in Quant. Electron.,2008,14:284-288. [19] CHEN C W,HSU Y K,HUANG J Y,et al.. Generation properties of coherent infrared radiation in the optical absorption region of GaSe crystal[J].Opt. Express,2006,14:10636-10644. [20] CHEN C W,TANG T T,LIN S H,et al.. Optical properties and potential applications ofε-GaSe at terahertz frequencies[J].J. Opt. Soc. Am. B,2009,26:A58-A65. [21] ZHANG Y F,WANG R,KANG Z H,et al.. AgGaS₂and Al doped GaSe for IR application[J].Opt. Commun.,2011,284:1677 1681. [22] ANDREEV Y M,VINNIK E M,LANSKII G V,et al.. Generation of tunable THz emission in solid solution GaSe_1-xTe_xcrystals[C]//Eight Siberian Conference on Climate and Ecological Monitoring,Oct 8-10,2009,Tomsk,Russia,2009:380-381.(in Russian) [23] ANDREEV Y M,VINNIK E M,LANSKII G V. Layered compound semiconductor GaSe and GaTe crystals for THz applications[J].Mater. Res. Soc. Symp. Proc.,2007,969:W03-W15. [24] LUO C W,KU S A,CHU W C,et al.. Physical property of the crystals grown from GaSe∶AgGaSe₂melt and application in Mid-IR facilities[C]//Int. Conference, Atomic and Molecular Pulsed,Sept 12-16,2011,Tomsk,Russia,2011:117. [25] SARKISOV S Y,NAZAROV M M,SHKURINOV A P,et al.. GaSe_1-xS_xand GaSe_1-xTe_xsolid solutions for terahertz generation and detection[C]//34^thInt. Conf. on Infrared,Millimeter and Terahertz wave(IRMMW-THz-2009),Sept 21-25,2009,Busan,South Korea,2009. [26] DAS S,GHOSH C,VOEVODINA O G,et al.. Modified GaSe crystal as a parametric frequency converter[J].Appl. Phys. B,2006,82:43-46. [27] ANDREEV Y M,ATUCHIN V V,LANSKII G V,et al.. Growth,real structure and applications of GaSe_1-xS_xcrystals[J].Mat. Sci. Eng. B,2006,128:205-210. [28] WANG T J,GAO J C,ANDREEV Y M,et al.. GaSe_1-xS_xsolid solutions[J].Rus. Phys. J.,2007,50:560-565. [29] QU Y,KABF Z H,WANG T J,et al.. GaSe_1-xS_xsecond harmonic generators for CO₂lidars[J].Atmos. Oceanic Opt.,2008,21:146-151. [30] KU S A,LUO C W,LIO H L,et al.. Optical properties of nonlinear solid solution GaSe_1-xS_x(0<x≤0.4) crystals[J].Rus. Phys. J.,2008,51:1083-1089. [31] MAYER G V,KOPYLOVA T N,ANDREEV Y M,et al.. Parametrical conversion of the frequency of organic lasers into the middle-IR range of the spectrum[J].Rus. Phys. J.,2009,52:640-645. [32] CHU L L,ZHANG I F,KANG Z H,et al.. Phase matching for the second harmonic generation in GaSe crystals[J].Rus. Phys. J.,2011,53:1235-1242. [33] ANDREEV Y M,KOKH K A,LANSKII G V V,et al.. Structural characterization of pure and doped GaSe by nonlinear optical method[J].J. Cryst. Growth,2011,318:1164-1166. [34] HAYEK M,BRAFMAN O,LIETH R M A. Splitting and coupling of lattice modes in the layer compounds GaSe, GaS, and GaSe_xS_1-x[J].Phys. Rev. B,1973,8:2772-2779. [35] VTODIEV I,LEONTIE L,CARAMAN M,et al.. Optical properties of p-GaSe single crystals doped with Te[J].J. App. Phys.,2009,105:023524. [36] YOSHIDA H,NAKASHIMA S,MITSUISHI A. Phonon Raman spectra of layer compound GaSe[J].Phys. Stat. Sol.(b),1973,59:655-666. [37] MAMEDOV G M,KARABULUT M,ERTAP H,et al.. Exciton photoluminescence, photoconductivity and absorption in GaSe_0.9Te_0.1alloy crystals[J].J. Lumines.,2009,129:226-230. [38] ABDULLAEV G B,ALLAKHVERDIEV K R,BABAEV S S,et al.. Raman scattering from GaSe_1-xTe_x[J].Solid State Commun.,1980,34:125-128. [39] SHIGETOMI S,IKARI T. Optical and electrical characteristics of p-GaSe doped with Te[J].J. Appl. Phys.,2004,95:6480-6482. [40] MENESES E A,JANNUZZI N,FREITAS J R,et al.. Photoluminescence of layered GaSe_1-xTe_xcrystals[J].Phys. Stat. Sol.(b),1976,78:K35-K38.}